Aung Metals, a reputable manufacturer and supplier located in Naypyidaw, Myanmar, has built a solid reputation for providing top-notch 1035 Round Bars that cater to a variety of industrial needs. Thanks to their cutting-edge production technology and rigorous quality control measures, Aung Metals guarantees that each 1035 Round Bar boasts exceptional strength, precision, and durability. Their unwavering commitment to quality has established them as a trusted source for carbon steel products in the engineering, manufacturing, and construction industries. The 1035 Round Bars from Aung Metals are particularly appreciated for their well-rounded mechanical properties, ease of machining, and reliable performance in applications that require moderate strength and resistance to wear.
These 1035 Round Bars are made from medium carbon steel, containing roughly 0.32–0.38% carbon, 0.60–0.90% manganese, up to 0.04% phosphorus, and 0.05% sulfur. This carefully balanced composition results in good hardness, tensile strength, and wear resistance, while still allowing for decent ductility and machinability. In terms of mechanical properties, 1035 steel typically has a tensile strength of about 620 MPa and a yield strength of around 350 MPa. It can also be heat-treated to enhance its hardness and strength, making it a great choice for components that need both durability and moderate formability.
|
Element |
Content |
|---|---|
|
Carbon, C |
0.310 – 0.380 % |
|
Iron, Fe |
98.63 – 99.09 % |
|
Manganese, Mn |
0.60 – 0.90 % |
|
Phosphorous, P |
0.040 % |
|
Sulfur, S |
0.050 % |
|
Properties |
Metric |
Imperial |
|---|---|---|
|
Tensile strength, ultimate |
585 MPa |
84800 psi |
|
Tensile strength, yield |
370 MPa |
53700 psi |
|
Modulus of elasticity |
190-210 GPa |
29700-30458 ksi |
|
Bulk modulus (typical for steel) |
140 GPa |
20300 ksi |
|
Shear modulus (typical for steel) |
80 GPa |
11600 ksi |
|
Poissons ratio |
0.27-0.30 |
0.27-0.30 |
|
Elongation at break (in 50 mm) |
30% |
30% |
|
Reduction of area |
53% |
53% |
|
Hardness, Brinell |
183 |
183 |
|
Hardness, Knoop (converted from Brinell hardness) |
204 |
204 |
|
Hardness, Rockwell B (converted from Brinell hardness) |
89 |
89 |
|
Hardness, Vickers (converted from Brinell hardness) |
192 |
192 |
|
Machinability (based on AISI 1212 steel. as 100 machinability) |
65 |
65 |
| EN Name | EN Number | DIN | JIS | UNI | BS |
|---|---|---|---|---|---|
| C35 | 1.0501 | C35, CM35 | S35C | C35 | 970 070M36 |
1035 Round Bar is not recommended for cryogenic applications as it may become brittle at extremely low temperatures.
To choose the right 1035 Round Bar, consider factors like the required strength, machinability, and specific application needs, ensuring it aligns with your project’s requirements.
Yes, 1035 Round Bar is recyclable and can be reused in various applications.
You’ll find 1035 Round Bars being widely utilized in sectors like automotive, engineering, and machinery manufacturing. They’re perfect for crafting components such as shafts, bolts, axles, crankshafts, couplings, and pins, where a balance of strength and machinability is essential. Additionally, these bars are used in agricultural equipment, fasteners, and various mechanical parts that require toughness and wear resistance. Thanks to their excellent response to heat treatment, 1035 Round Bars are often the go-to choice for forging and machining tasks. Their versatility, cost-effectiveness, and reliable performance make them a favored material for medium-strength engineering and structural applications.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Aung Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Naypyidaw, Myanmar
Copyright 2024 Aung Metals. All rights reserved